摘要：

The amounts of adsorption of Cu²⁺, Ni²⁺, and Zn²⁺ from single, binary, and tertiary nitrate solutions onto glutaraldehyde cross-linked chitosan beads were measured. The beads had an average particle size and pore volume of 2 mm and 0.06 cm³/g, respectively, and had a BET surface area of 60 m²/g. All experiments were performed at 298 K as a function of initial pH (2.0–5.0), total metal concentration (0.77–17.0 mol/m³), and molar concentration ratio (0.25–4) in the aqueous phase. It was shown that the amount of metal adsorption generally increased with increasing solution pH. Competitive adsorption was significant in binary and tertiary systems when Cu²⁺ was present. The selectivity factor reached maximum in an equilibrium pH range of 5.1–5.3 and 4.5–4.9 for the Cu-Ni and Cu-Zn binary systems, respectively. This adsorbent provided a possibility for selective separation of Cu²⁺ from such multi-componen