We look forward for an eco-friendly hydrocarbon polymer with higher molecular weight for the preparation of an anion exchange membrane. Polystyrene ethylene butylene polystyrene (PSEBS) was chosen as the polymer matrix. The anion exchange membrane was prepared from PSEBS tri-block co-polymer and then the properties were characterized for alkaline fuel cell application. The preparation of anion exchange polymer involved two steps namely chloromethylation and quaternization. The anion exchange membrane with high conductivity has been prepared by introducing quaternary ammonium groups in to the polymer. Finally, the membrane was prepared using solution casting method. The solution casting method yields highly hydrophilic membranes with uniform structure that were suitable for electrochemical applications. The efficiency of the entrapment was monitored by swelling ratio, chemical stability and ion exchange measurement. The characteristic structural properties of the membrane were investigated by FT-IR spectroscopy and 1H NMR spectroscopy. The thermal stability of the membrane was characterized by TGA, DSC and DMA (dynamic mechanical analysis). The prepared uniform electrolyte membrane in this study has high thermal and chemical stability. The surface morphology and elemental composition of the quaternized PSEBS was determined by SEM-EDXA techniques, respectively. The measured hydroxyl ion conductivity of the synthesized alkaline PSEBS polymer electrolyte membrane showed ionic conductivity in the range of 10 3 S/cm in deionized water at room temperature. It was found that the substitution provided a flexible, chemically and thermally stable membrane. Hence, the membrane will have potential application in the alkaline fuel cell.

展开