Photo and temperature cured polymer dielectrics could be fabricated on a gate-patterned glass, with two immiscible polymer precursors, divinyltetramethyldisiloxane-bis(benzocyclobutene) (BCB precursor) and poly(melamine-co-formaldehyde)acrylate (PMFA), which have excellent insulating properties, but show discernible dielectric constants and polarities. On hydrophobic BCB-assisted PMFA blend dielectrics (approximately 400 nm thick), organic field-effect transistors (OFET) and complementary inverters were demonstrated using pentacene andN,N′-ditridecylperylene-3,4,9,10-tetracarboxylic diimide (PTCDI-C13) as semiconducting channels. The values of field-effect mobilities showed up to 0.33 cm2V1s1(for pentacene) and 0.85 cm2V1s1(for PTCDI-C13), respectively. In addition, these based complementary inverter was successfully demonstrated with a high voltage gain ofca.41, specifically, onto the 10 wt% BCB-assisted PMFA dielectric optimized to achieve a hydrophobic and smooth surface by vertically phase-separating the immiscible polymers.